性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 比重 | ASTM D-792 | 1.05 | ||
模具收縮率 | ASTM D-955 | 0.4-0.7 | % | ||
熔融指數(shù) | 220℃/10kg | ASTM D-1238 | 5 | g/10min | |
機(jī)械性能 | 拉伸強(qiáng)度 | 50mm/min | ASTM D-638 | 500 | kg/cm |
伸長率 | 50mm/min | ASTM D-638 | 30 | % | |
抗彎強(qiáng)度 | 15mm/min | ASTM D-790 | 740 | kg/cm | |
抗彎模數(shù) | 15mm/min | ASTM D-790 | 23000 | kg/cm | |
IZOD缺口沖擊強(qiáng)度 | Notched 1/4" | ASTM D-256 | 15 | kg.cm/cm | |
Notched 1/8" | ASTM D-256 | 18 | kg.cm/cm | ||
洛氏硬度 | ASTM D-785 | 106 | R-scale | ||
熱性能 | 熱變形溫度 | 18.5kg/cm | ASTM D-648 | 104 | ℃ |
維卡軟化點(diǎn) | 1000g | ASTM D-1525 | 125 | ℃ |